The use of titania (TiO2) nanotubes is becoming one of the most attractive techniques as surface treatment for implants due its combination of morphology (that accelerates osteoblast adhesion and proliferation), bioactivity and possibility of being use as a drug vehicle. Anodic oxidation is one of the cheapest and simplest approaches to obtain highly ordered nanotubes. Parameters such as applied potential, reaction time and fluoride containing in the electrolyte define the nanotubes morphology. However, the mechanical properties of the nanotubes layer do not have been completely elucidated and they play a crucial role in the implant long term stability. The objective of this research was to obtain TiO2nanotubes using anodic oxidation and to determine their elastic modulus and hardness. The TiO2nanotubes layer was obtained in a fluoride containing electrolyte for 1 hour, one group at 15 V and another one at 25 V. The TiO2nanotubes morphology was characterized by scanning electron microscopy (SEM) and atomic force microscopy (AFM). The elastic modulus and hardness were evaluated by nanoindentation experiments using a spherical tip. SEM images showed highly ordered nanotubes on all titanium surfaces and it was observed that the nanotubes diameters are directly related with the applied potential. Nanotubes diameters are 66 ± 9 nm and 131 ± 22 nm for nanotubes obtained at 15 V and 25 V, respectively. Nanoindentation test results showed a decrease in the elastic modulus comparing with titanium reference and these values approach to cortical bone elastic modulus. These results demonstrate that it was possible to obtain a homogeneous TiO2nanotubes layer that has mechanical properties adequate to improve implant long-term stability.

Gamma and ultraviolet radiation effects on hardness, elastic modulus and viscoelastic properties of polyurethane derived from castor oil (PU) were investigated by nanoindentation tests. Modifications on surface morphology, induced by radiation, were observed by atomic force microscopy. The polyurethane derivate from castor oil shows good resistance to gamma radiation, with only small changes in hardness, elastic modulus, viscoelastic properties and contact angle. The hardness of PU increases at the near surface region due to UVA radiation and decreases after UVC radiation. The contact angle for water drop decreases after UVC radiation, but not after gamma radiation, despite a significant increase in roughness. Such results are attributed to different responses from polyurethane to radiation energy. Increase in hardness due to UVA is attributed to a higher crosslinking at shallow depths, while a decrease in mechanical properties may be attributed to chain scission. These results are consistent with the modifications on viscoelastic properties. Shore D hardness did not show the same trend as observed by nanoindentation results. Hardness, viscoelastic properties and contact angle of castor oil polyurethane are more severely influenced by UVC radiation, while gamma radiation does not have a significant effect.

Neste trabalho são investigadas as propriedades mecânicas de poliuretana derivada do óleo de mamona, utilizando a técnica de indentação instrumentada com penetradores de geometrias piramidal e esférica. Foi analisada a influência da forma do penetrador utilizado nos ensaios de indentação instrumentada para se obter valores das propriedades mecânicas de polímero derivado de óleo de mamona. Os penetradores utilizados são de pontas piramidais dos tipos Berkovich e canto de cubo e esférico de raio igual a 150 μm em um Nanoindenter XP TM com cargas aplicadas entre 1 e 200 mN. As penetrações variam de acordo com o formato do penetrador, sendo maiores para pontas agudas. A dureza e o módulo de elasticidade foram determinados, utilizando o método de Oliver e Pharr. Verificou-se que os valores medidos para a dureza são maiores para penetradores mais agudos. Os valores obtidos com a ponta piramidal Berkovich foram de 0,14 GPa para pequenas penetrações e 0,12 GPa para maiores penetrações. Já os valores obtidos com ponta canto de cubo foram 25 a 30% maiores. Isso está relacionado com os volumes das regiões que apresentam deformações plásticas elevadas, no caso de penetradores agudos comparados com os volumes das regiões que sofrem deformações viscoelásticas. A viscosidade aparente determinada, utilizando penetrador esférico em testes de força aplicada constante, é igual a (22 ± 2) × 10(12) Pa.s.

The mechanical properties of polyurethane derived from castor oil, obtained by instrumented indentation technique with pyramidal and spherical indenters are reported. The influence of the indenter shape on the values of mechanical properties of the polymer was investigated. The indentations were made with pyramidal Berkovich, cube corner and a spherical indenter with radius of 150 μm in a Nanoindenter XP TM. The applied loads varied between 1 and 200 mN. The penetration depth increases for acute indenters, being higher for the cube corner tip. The hardness and elastic modulus were determined using the method of Oliver and Pharr. It was found that the measured values for hardness are higher for more acute indenters. The hardness with the pyramidal Berkovich tip was 0.14 GPa for small penetrations and 0.12 GPa for higher penetration depths. The values obtained with a cube corner tip were 25 to 30% higher. This is related to the volumes of regions with high plastic deformation in the case of acute indenters compared to the volumes of regions that present viscoelastic deformation. The apparent viscosity determined using the spherical indenter, in tests with applied constant forces, is equal to (22 ± 2) × 10(12) Pa.s.